Engineering Properties
| Property | units | Parylene C |
Parylene N |
Parylene D |
ASTM method |
|---|---|---|---|---|---|
| General | |||||
| Density | g/cm3 | 1·29 | 1·11 | 1·42 | D1505 |
| Refractive Index | ηd23 | 1·64 | 1·66 | 1·67 | |
| Mechanical | |||||
| Tensile Modulus | GPa | 3·2 | 2·4 | 2·8 | D882 |
| Tensile Strength | MPa | 70 | 45 | 75 | D882 |
| Yield Strength | MPa | 55 | 42 | 60 | D882 |
| Elongation to Break (un-aged) | % | 200 | 30 | 10 | D882 |
| Yield Elongation | % | 2·9 | 2·5 | 3 | D882 |
| Rockwell Hardness | °R | 80 | 85 | D785 | |
| Coefficient of Friction - static | 0·29 | 0·25 | 0·35 | D1894 | |
| - dynamic | 0·29 | 0·25 | 0·31 | D1894 | |
| Thermal | |||||
| Melting Point | °C | 290 | 420 | 380 | |
| Thermal Conductivity | W/m.K | 0·08 | 0·12 | ||
| Electrical | |||||
| Dielectric Constant - 50 Hz | 3·15 | 2·65 | 2·84 | D150 | |
| - 1 kHz | 3·10 | 2·65 | 2·82 | D150 | |
| - 1 MHz | 2·95 | 2·65 | 2·80 | D150 | |
| Dissipation Factor - 50 Hz | 20.10-3 | 0·2.10-3 | 4.10-3 | D150 | |
| - 1 kHz | 19.10-3 | 0·2.10-3 | 3.10-3 | D150 | |
| - 1 MHz | 13.10-3 | 0·6.10-3 | 2.10-3 | D150 | |
| Dielectric Strength @ 25μ - short time | MV/m | 220 | 275 | 215 | D149 |
| - step-by-step | 185 | 235 | D149 | ||
| Resistivity @ 23°C, 50%RH - Volume | Ω | 8·8.1016 | 1·4.1017 | 2.1016 | D257 |
| - Surface | Ω | 1.1014 | 1.1013 | 5.1016 | D257 |
| Barrier | |||||
| Water Absorption | % | <0·1 | <0·1 | <0·1 | D570 |
| Water Vapour Transmission @ 37°C | ng/(Pa.s.m) | 0·4.10-3 | 1·2.10-3 | 0·2.10-3 | E96 |
| Gas Permeability @ 25°C - N2 | amol/(Pa.s.m) | 2·0 | 15·4 | 9·0 | D1434 |
| - O2 | 14·4 | 78·4 | 64·0 | D1434 | |
| - CO2 | 15·4 | 429 | 26·0 | D1434 | |
| - H2S | 26·0 | 1590 | 2·9 | D1434 | |
| - SO2 | 22·0 | 3790 | 9·5 | D1434 | |
| - Cl2 | 0·7 | 148 | 1·1 | D1434 | |
 |
|||||